The importance of heat treatment

The importance of heat treatment

When casting or forging metal parts, several factors will influence the final properties of the material. These processes have an effect on the material’s internal condition of the material, e.g., the shape and dimension of the grain structure, the distribution of the alloying elements and the presence of unwanted chemical reactions.

An essential step in the production of good materials is the heat treatment process. During the heat treatment, the material is heated up in a furnace at a pre-defined temperature for a prescribed time, after which it is cooled down in a prescribed way. There are many materials, and just as many heat treatment processes. Along with the chemical elements that the material contains (such as C, Mn, Cr and Ni), the heat treatment will determine the strength of the material and its chemical behaviour.

Common heat treatment processes

  • Normalising (+N) carbon steel (e.g., G20Mn5): the material is heated to 925°C for two hours and then air cooled.
  • Quenching and tempering (+QT) of low alloy steel (e.g., G42CrMo4): the material is heated to 925°C for two hours, then quickly cooled in water or oil. The result is a very hard and brittle material. After quenching, the material is softened by a tempering process at +/- 600°C.
  • Solution annealing and quenching (+AT) for stainless steel (e.g., GX5CrNi19-10). The material is heated to 1,100°C for two hours, after which it is quickly cooled in water.

Let's work together

Want to know what we can deliver? Let us know about your project!

Tell us about your project
Flag of Belgium Belgium
+32 14 44 37 80
Flag of China China
+86 311 87 76 55 50
Flag of Denmark Denmark
+45 98 920 65 6
Flag of Finland Finland
+358 40 028 86 31
Flag of Germany Germany
+49 71 539 28 63 56
Flag of Poland Poland
+48 12 361 21 06
Flag of Sweden Sweden
+46 85 197 06 55
Flag of The Netherlands The Netherlands
+31 78 654 47 77